| 类型：其他 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % | |
| 物理性能 | 比重 | JIS K-7112 | 1.20 | |||
| 折射率 | ASTM D-542 | 1.585 | ||||
| 阻燃性 | 0.38mm | UL 94 | V-2 | |||
| 透光率 | 3mm thick | ASTM D-1003 | 88 | % | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 77 | M标度 | ||
| 压缩强度 | ASTM D-695 | 76(780) | Mpa(kgf/cm2) | |||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 130(13) | J/m(kgf· cm/cm) | ||
| 拉伸率 | 屈服点 | ASTM D-638 | 6 | % | ||
| 断裂点 | ASTM D-638 | 140 | % | |||
| 拉伸模量 | ASTM D-638 | 2130(21700) | Mpa(kgf/cm2) | |||
| 弯曲强度 | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |||
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 830(85) | J/m(kgf· cm/cm) | ||
| 拉伸强度 | 屈服点 | ASTM D-638 | 62(630) | Mpa(kgf/cm2) | ||
| 断裂点 | ASTM D-638 | 78(800) | Mpa(kgf/cm2) | |||
| 弯曲模量 | ASTM D-790 | 2260(23000) | Mpa(kgf/cm2) | |||
| 电气性能 | 介电率 | 60Hz | ASTM D-150 | 2.95 | ||
| 体积电阻率 | ASTM D-257 | 3×1016 | Ω.cm | |||
| 介电正切 | 60Hz | ASTM D-150 | 0.0004 | |||
| 耐电弧性 | ASTM D-495 | 110 | sec | |||
| 耐导电径迹性（CTI） | IEC 112 | 300 | V | |||
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | |||
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||
| 介电率 | 106Hz | ASTM D-150 | 2.9 | |||
| 加工性能 | 成型收缩率 | 流动方向 | ASTM D-955 | 0.5～0.7 | % | |
| 垂直方向 | ASTM D-955 | 0.5～0.7 | % | |||
| 热性能 | 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 142 | ℃ | |
| 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | °C | |
| 冲击式 | 厚度1.47mm | UL 746B | 115 | °C | ||
| 非冲击式 | 厚度1.47mm | UL 746B | 125 | °C | ||
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 132 | ℃ | ||
| 线膨胀系数 | 流动方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | ||
| 垂直方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | |||